How to prolong the service life of stamping die steel (what types of stamping die steel are there)

冲压模具钢是冷冲压中将材料加工成零件的专用工艺设备。由于冲压模具在生产过程中经常磨损，工作尺寸会出现误差，使用寿命会缩短，难以满足生产要求。因此，提高金属冲压模具的耐久性是提高其使用寿命和经济效益的关键。接下来模具钢厂家就和大家分享一下如何提高冲压模具钢的使用寿命。

Stamping die steel is a special process equipment for processing materials into parts in cold stamping. Because the stamping die is often worn in the production process, the working size will have errors and the service life will be shortened, which is difficult to meet the production requirements. Therefore, improving the durability of metal stamping die is the key to improve its service life and economic benefits. Next, die steel manufacturers will share with you how to improve the service life of stamping die steel.

1.冲压模具的设计是关键

1. The design of stamping die is the key

冲压模具设计合理与否，直接关系到冲压模具的耐久性。因此，在设计冲压模具时，应采取措施应对产品成形中的不利条件，以提高冲压模具的耐久性。对于这种冲压模具，小凸模的设计应尽可能缩短其长度，以增加其强度。同时应采用导套法加强小凸模进行保护。

Whether the design of stamping die is reasonable or not is directly related to the durability of stamping die. Therefore, when designing stamping die, measures should be taken to deal with the adverse conditions in product forming, so as to improve the durability of stamping die. For this kind of stamping die, the design of small punch should shorten its length as much as possible to increase its strength. At the same time, the guide sleeve method should be used to strengthen the protection of small punch.

2.冲压模具材料的选择要正确

2. The selection of stamping die materials should be correct

不同的冲压模具材料具有不同的强度、韧性和耐磨性。在一定条件下，使用高材料可以使耐用性提高几倍。所以，要想提高冲压模具的耐用性，就要选择正规工厂生产的材料。

Different stamping die materials have different strength, toughness and wear resistance. Under certain conditions, the durability can be improved several times by using high-quality materials. Therefore, in order to improve the durability of stamping dies, we must choose the materials produced by regular factories.

3.冲压模具零件的锻造和热处理应合理

3. The forging and heat treatment of stamping die parts shall be reasonable

在选择冲压模具材料的同时，对同种材料不同性能的材料要求合理的锻造和热处理，是提高冲压模具耐久性的主要途径之一。比如淬火时，如果加热时生产过热，不仅会使工件太脆，而且冷却时容易变形开裂，降低耐久性。因此，在制造冲压模具时，一定要合理掌握热处理工艺。

One of the main ways to improve the durability of the same kind of forging die is to reasonably select different stamping materials at the same time. For example, during quenching, if the production is overheated during heating, it will not only make the workpiece too brittle, but also easy to deform and crack during cooling, reducing durability. Therefore, when manufacturing stamping dies, we must reasonably master the heat treatment process.

以上就是为大家介绍的有关冷作模具钢https://www.jnqhmj.com的详细介绍,希望对您有所帮助.如果您有什么疑问的话,欢迎联系我们.我们将以的态度,为您提供服务

The above is about cold working die steel introduced to you https://www.jnqhmj.com I hope it will be helpful to you If you have any questions, please contact us We will provide you with professional service